The interactions of Sn and S and their effects on the magnetic properties of non-oriented silicon steel sheets were discussed in reference to industrial production. Results show that minor amounts of Sn can improve magnetic induction sharply but have little effect on core loss when the S content is below 10 × 10 ^-4%. The precipitation of AlN can be restrained effectively by Sn. Sn, as the nucleus, can remove some of the inclusions with a size of 0.5μm or larger, but has little effect on inclusions smaller than 0.5 μm,which is the key factor affecting core loss. Sn improves the magnetic induction of finished steel sheets mainly through the change of the steel texture. The relationship between the magnetic induction and Sn and S content can be regressed as B50 = 1.69 -4.37 ws +0.30 Ws,. From the regression formulation,the magnetic induction can be improved by 0.03 T when 0.01% Sn is added under relatively low S content conditions.
The interactions of Sn and S and their effects on the magnetic properties of non-oriented silicon steel sheets were discussed in reference to industrial production. Results show that minor amounts of Sn can improve magnetic induction sharply but have little effect on core loss when the S content is below 10 × 10 ^-4%. The precipitation of AlN can be restrained effectively by Sn. Sn, as the nucleus, can remove some of the inclusions with a size of 0.5μm or larger, but has little effect on inclusions smaller than 0.5 μm,which is the key factor affecting core loss. Sn improves the magnetic induction of finished steel sheets mainly through the change of the steel texture. The relationship between the magnetic induction and Sn and S content can be regressed as B50 = 1.69 -4.37 ws +0.30 Ws,. From the regression formulation,the magnetic induction can be improved by 0.03 T when 0.01% Sn is added under relatively low S content conditions.