采用四羟甲基氯化磷(THPC)对无机蒙脱土(MMT)进行有机化改性,制备了有机蒙脱土(OMMT)。在此基础上,采用树枝形聚合物改性技术对OMMT进一步改性,制备了不同代数的树枝形有机蒙脱土(DOMMT)。采用硼酸对其进行封端,制备了树枝形有机蒙脱土阻燃剂(FR-DOMMT)。通过红外光谱(FTIR)、热失重(TGA)、X-衍射(XRD)及扫描电镜(SEM)等手段分析了不同材料的结构与性能。结果表明,经过有机化和树枝形聚合物改性后的蒙脱土表面的官能团、层间距以及热稳定性均有不同程度的改变或提高。
Montmorillonite (MMT) was orgaoic^dly modified by tetrakis hydroxymethyl phosphonium chloride (THPC) to produce organic montmorillonite (OMMT) . Dendrimer modifi- cation technology was used to modify OMMT. and dendrimer type of OMMT (DOMMT) with different generations was ob rained. This DOMMT was terminated by boric acid to prepare flame-retardant dendrimer type of OMMT (FR-DOMMT) . These materials were characterized by FTIR. TGA, XRD. and SEM. The results showed that the surface functional groups, in- terlayer spacing and thermal stability were changed or improved at different degrees.
出处
《化工矿物与加工》
CAS
北大核心
2013年第7期14-17,共4页
Industrial Minerals & Processing
基金
国家自然科学基金项目(51173102
51210105020)
上海市曙光计划项目(10SG53)
上海市人才发展资金项目((2012)No.23)
上海工程技术大学校基金(2012td10
2012zh05)
天然源制药工程学科及创新团队建设项目(XKCZ1205)
上海市科委地方高校能力建设项目(11490501500)
国家级大学生创新创业训练计划项目(201210856021)
上海工程技术大学大学生创新创业计划项目资助(cx1204001
cs1204007和cy1204003)
关键词
蒙脱土
树枝形聚合物
结构
性能
montmorillonite
dendrimer
structure
property