制备了高密度聚乙烯(HDPE)接枝马来酸酐(MAH)粘接树脂,进一步对接枝工艺进行研究。结果表明,MAH的含量、过氧化二异丙苯(DCP)的含量、共混时间都会对粘接效果产生影响。共混时间为8 min时,接枝反应已经很充分;当添加1.5份MAH和0.1份DCP时,接枝率达到最大值0.815%,此时综合粘接效果最好。
HDPE grafted studied. The result found that adhesive property. The MAH, DCP reached 1. and the comprehensive maleic anhydride adhesive resin was prepared. The grafting technology was the content of maleic anhydride and DCP, as well as time had an effect on the grafting reaction carried out fully when mixing time reached at 8 min, when content of 5 phr and 0. 1 phr respectively, the grafting ratio reached at the maximum 0. 815%, adhesive property was the best.