Nanocrystalline MgO with a relatively high surface area and mesoporous structure was synthesized by a surfactant assisted precipitation method for use as the support of nickel catalysts for steam reforming of methane. The samples were characterized by X‐ray diffraction, N2 adsorption, temperature‐programmed reduction, temperature‐programmed oxidation, scanning electron microscopy, and transmission electron microscopy. The catalysts showed high catalytic activity and good stability in the steam reforming of methane. Increasing the nickel loading up to 10 wt% gave increased activity. Catalysts with higher nickel loadings showed more deposited carbon after reaction. The excellent anti‐coking performance of the catalysts was attributed to the formation of a nickel‐magnesia solid solution, basicity of the support surface, and nickel‐support interaction.
Nanocrystalline MgO with a relatively high surface area and mesoporous structure was synthesized by a surfactant assisted precipitation method for use as the support of nickel catalysts for steam reforming of methane. The samples were characterized by X‐ray diffraction, N2 adsorption, temperature‐programmed reduction, temperature‐programmed oxidation, scanning electron microscopy, and transmission electron microscopy. The catalysts showed high catalytic activity and good stability in the steam reforming of methane. Increasing the nickel loading up to 10 wt% gave increased activity. Catalysts with higher nickel loadings showed more deposited carbon after reaction. The excellent anti‐coking performance of the catalysts was attributed to the formation of a nickel‐magnesia solid solution, basicity of the support surface, and nickel‐support interaction.
出处
《催化学报》
SCIE
CAS
CSCD
北大核心
2013年第7期1443-1448,共6页
基金
supported by Islamic Azad University,Omidiyeh Branch