摘要
对纤维增强树脂基复合材料加筋板进行了剪切试验,结合应变-剪切力曲线对加筋板的破坏形式以及屈曲特性进行了研究。结果表明:加筋板的破坏形式主要表现为筋条脱胶、断裂和蒙皮撕裂;蒙皮达到局部屈曲后,加筋板仍具有较大的后屈曲承载能力,其破坏载荷约为屈曲载荷的4.5倍。
Shear experiments were performed on fiber-reinforced resin matrix composite stiffened panels, and the failure pattern and buckling characteristics of stiffened panel were studied via strain-shear stress curves. The results show that the failure modes of stiffened panels mainly were the debonding and cracking of stiffener and tearing of skin. After skin was local buckling, the stiffened panel still had larger post-buckling carrying capacity, and the failure load of the stiffened panel was about 4, 5 times higher than that of the buckling load.
出处
《机械工程材料》
CAS
CSCD
北大核心
2013年第7期82-84,97,共4页
Materials For Mechanical Engineering
关键词
纤维增强树脂基复合材料
加筋板
剪切
承载能力
局部屈曲
后屈曲
fiber-reinforced resin matrix composite
stiffened panel
shear
caryying capacity
local buckling
post-buckling