高桩码头面层混凝土很容易出现裂缝,为了减小或避免裂缝的产生,在对码头地面混凝土裂缝调查检测的基础上,结合温度应力计算、干缩应力计算,对码头面层混凝土裂缝原因进行了深入分析,阐明了产生裂缝的根本原因,并据此提出了相应的裂缝控制技术措施。
The high pile wharf surface layer concrete is very easy to appear the crack,in order to reduce or avoid the crack the production,the wharf ground concrete crack investigation examination foundation in,the union temperature stress computation,the air shrinkage stress computation,has carried on the thorough analysis to the wharf surface layer concrete crack reason,had expounded has the crack basic reason,according to the above and proposed the corresponding crack control technology measure.