主要介绍普碳钢高速线材表面结疤产生的原因,通过采取稳定连铸拉速,降低钢水过热度,提高钢水质量、连铸操作水平等措施,解决了高速线材表面结疤的问题。
This paper mainly introduces the reasons for surface scar of carbon - steel high speed wire rod. Measures like ： a- dapting stable pull speed, reducing the liquid steel superheat degree, improving the quality of molten steel and continuous casting opera- tion level are taken to solve the problem of scarring defect.