摘要
Poly[2,2-(m-phenylene)-5,5-bibenzimidazole](mPBI)were synthesized by mixing 3,3',4,4'-tetraaminobiphenyl and isophthalic acid in 1-butyl-3-methylimidazolium chloride([BMIM]Cl).Intrinsic viscosity of mPBI polymers was 0.67 dL/g which was measured in 96%sulfuric acid.The polymer was characterized by Fourier transform infrared spectroscopy(FTIR),nuclear magnetic resonance(1H-NMR),and thermogravimetric analysis(TGA).The effects of polymerization conditions on the intrinsic viscosity of mPBI were investigated.It showed that the molecular weight of polymer mainly depended on pre-reaction time and reaction temperature.Comparison of structure and properties of mPBI synthesized in ionic liquids(ILs)and polyphosphoric acid was also reported.It indicates that the ionic liquids are a kind of good solvents in synthesis process of mPBI and ionic liquids mainly affect molecular weight of mPBI.
Poly[ 2, 2-（m.phenylene） -5, 5-bibenzimidazole] （mPBI） were synthesized by mixing 3, 3＇, 4, 4＇-tetraaminobiphenyl and isophthallc acid in 1 -butyl-3 -methyUmidazolinm chloride （ E BMIM] CI）. Intrinsic viscosity of mPBI polymers was 0.67 dL/g which was measured in 96% sulfuric acid. The polymer was characterized by Fourier transform infrared spectroscopy （FTIR）, nuclear magnetic resonance （ 1H-NMR ）, and thermogravimetric analysis （TGA）. The effects of polymerization conditions on the intrinsic viscosity of mPBI were investigated. It showed that the molecular weight of polymer mainly depended on pre-reaction time and reaction temperature. Comparison of structure and properties of mPBI synthesized in ionic liquids（ILs） and polyphosphoric acid was also reported. It indicates that the ionic liquids are a kind of good solvents in synthesis process of m_PBI and ionic liquids mainly affect molecular weight of mPBL
基金
Natural Science Foundation of Shanghai,China(No.09ZR1401500)
关键词
化学
化学原理
化学方法
高分子化学
polybenzimidazole （ PBI ）
1-butyl-3-methylimidazolium chloride（ [ BMIM] C1 ）
ionic liquids（ILs）
synthesis