首钢京唐公司IF钢镀锌板表面夹杂物缺陷分析与控制

Analysis and Control of Surface Defects on IF Steel for Galvanized Steel Sheet of Shougang Jingtang Company
下载PDF
导出
摘要 分析了首钢京唐公司IF钢镀锌板表面夹杂物缺陷及IF钢连铸工艺。结果表明,开浇第2块连铸坯、换水前后连铸坯和连浇过渡坯夹杂物缺陷概率高是造成IF钢镀锌板表面夹杂物缺陷的主要原因。采取高频快涨的连铸机拉速控制、留钢操作、提高耐火材料质量、规范换水口前后化渣操作、大包水口浸入式开浇、RH炉化冷钢与洗槽、优化中间包结构以及连铸坯火焰清理等措施后,IF钢镀锌板表面夹杂物缺陷显著降低。 The surface defects and continuous casting process of IF steel for galvanized steel sheet of SGJT were analyzed. The results showed that the main reasons of the surface defects were the higher possibility of inclusions contents in the second slabs, nozzle-changed slabs and middle slabs. The IF steel surface defects were decreased remarkably through several measures such as steel-remaining, refractory quality improving, cold steel removing in RH and tundish structure opitimizing.
作者 黄俊
出处 《首钢科技》 2013年第4期24-28,共5页 Shougang Science and Technology
关键词 冷轧镀锌板 夹杂缺陷 分析 控制 cold rolled galvanizing sheet, surface Inclusions, analysis, control
  • 引文网络
  • 相关文献

参考文献2

二级参考文献11

  • 1赵辉,王先进.无间隙原子钢的生产与发展[J].钢铁研究,1993,21(1):49-54. 被引量:12
  • 2袁方明,王新华,李宏,任子平,张富强,孟劲松,孙群.不同浇铸阶段IF钢连铸板坯洁净度[J].北京科技大学学报,2005,27(4):436-440. 被引量:44
  • 3W H Emling, T A Waugaman, S L Feldbauer, et al. Subsurface mold slag entrapment in ultra low carbon steel[C].//77th Steelmaking Conference Proceedings. Chicago:1994, 371-379.
  • 4M Iguehi, J Yoshida, T Shimizu. Model study on the entrapment of mold powder into molten steel[J].ISIJ, Int,2000, 40 (7): 785-691.
  • 5K Tanizawa, Influence of the ,steelmaking conditions on nonmetallic inclusions and product defect[J]. ISIJ. Int,s,Metallurgia Italiana, 1992, 84(1 ) : 17-22.
  • 6Haizhou Wang. Original position statistic distribution analysis (Original Position Analysis)- new analytical method in the research and quality evaluation of materials[J]. Science in China (series B),2002, 32 (6):481-484.
  • 7Haizhou Wang. Several problems about the metallurgy analysis of 21th century[J]. Steel and Iron, 2000, 35 (1):73-78.
  • 8Haizhou Wang. The metallurgy material analysis toward new century[J]. LIHUA JIANYAN (Chemistry), 2001,37 (1):49-52.
  • 9Han Biao,He Feng,Ye H F K,Wang X F. Numerical simulation of transient flow with free surface in engineering[J].Journal of Hydrodynamica, 1999,14a(2):142-147.
  • 10Han Biao, Yao Zhaohui, Ye Hongkai, et al. 3-D numerical simulation on the vibration of liquid sodium S free surface in sodium pool of FBR[J]. Nuclear Power Engineering, 1997,18(3):211-216.

共引文献31

;
使用帮助 返回顶部