摘要
本文研究了石英纤维增强的聚三唑树脂复合材料的固化行为、热性能、介电性能及力学性能。复合材料能够在80℃下固化成型,经过120℃/2h+150℃/2h+180℃/2h+200℃/2h+250℃/2h后处理,固化完全,玻璃化转变温度T g高达230℃,介电常数为3.8。力学性能随后处理温度升高而上升,至250℃时,弯曲强度和层间剪切强度分别为795MPa和61MPa,180℃时弯曲强度保留率达到59%。
Curing behavior, thermal properties, dielectric properties and mechanical properties of quartz fiber reinforced polytriazole resin composites were investigated in this paper. The composites can be cured at 80℃, and Tg of one of the composites reaches 230℃ after the post-processing of 120℃/2h + 150℃/2h + 180~C/2h + 200℃/ 2h +250℃/2h. Dielectric constant of this composite is 3.8. Mechanical properties of the composites increase by the post-processing temperature. Flexural strength arrives at 795MPa after the post-processing at 250℃, which re- tention rate at 180℃ is 59%. Interlaminar shear strength is 61MPa at ambient temperature.
出处
《玻璃钢/复合材料》
CSCD
北大核心
2013年第6期J0013-J0016,共4页
Fiber Reinforced Plastics/Composites
关键词
石英纤维
聚三唑树脂
复合材料
力学性能
介电性能
quartz fiber
polytriazole resin
composites
mechanical properties
dielectric properties