摘要
Although addition of β-nucleating agent directly into homo-polypropylene （PPH） is a useful method to improve ,β-crystal content and toughen PPH, polypropylene random copolymer （PPR） makes this method powerless due to its random structure and low crystallinity. In this study, the β-nucleated PPR with high β-crystal content was prepared by a novel high effective β-nucleating system which consists of β-nucleation agent （TMB-5） and modified zeolite 13X （M13X）. It was found that M13X and TMB-5 had a synergistic influence on improving β-crystal content and toughening PPR. The content of β-crystal in PPR/M13X/TMB-5 was significantly larger than the sum of that in PPR/M13X and PPR/TMB-5. Besides, fracture behavior, phase morphology and relaxation of matrix chain segments were also investigated. The results showed that M13X and TMB-5 improved the mobility of amorphous chain segments at low temperature and contributed to much energy dissipation. This work provides a powerful method to modify PPR.
Although addition of β-nucleating agent directly into homo-polypropylene （PPH） is a useful method to improve ,β-crystal content and toughen PPH, polypropylene random copolymer （PPR） makes this method powerless due to its random structure and low crystallinity. In this study, the β-nucleated PPR with high β-crystal content was prepared by a novel high effective β-nucleating system which consists of β-nucleation agent （TMB-5） and modified zeolite 13X （M13X）. It was found that M13X and TMB-5 had a synergistic influence on improving β-crystal content and toughening PPR. The content of β-crystal in PPR/M13X/TMB-5 was significantly larger than the sum of that in PPR/M13X and PPR/TMB-5. Besides, fracture behavior, phase morphology and relaxation of matrix chain segments were also investigated. The results showed that M13X and TMB-5 improved the mobility of amorphous chain segments at low temperature and contributed to much energy dissipation. This work provides a powerful method to modify PPR.
基金
financially supported by the National Natural Science Foundation of China(No.50803042)
Chengdu Economic & Technological Development Zone and Chuanlu Group