摘要
Zn1-xMnxO （x = 0.0005, 0.001, 0.005, 0.01, 0.02） nanocrystals are synthesized by using a wet chemical process. The coordination environment of Mn is characterized by X-ray photoelectron spectroscopy, Raman spectroscopy, and its X-ray absorption fine structure. It is found that the solubility of substitutional Mn in a ZnO lattice is very low, which is less than 0.4%. Mn ions first dissolve into the substitutional sites in the ZnO lattice, thereby forming Mn2＋O4 tetrahedral coordination when x ≤ 0.001, then entering into the interstitial sites and forming Mn3＋O6 octahedral coordination when x ≥ 0.005. All the samples exhibit paramagnetic behaviors at room temperature, and antiferromagnetic coupling can be observed below 100 K.
Zn1-xMnxO （x = 0.0005, 0.001, 0.005, 0.01, 0.02） nanocrystals are synthesized by using a wet chemical process. The coordination environment of Mn is characterized by X-ray photoelectron spectroscopy, Raman spectroscopy, and its X-ray absorption fine structure. It is found that the solubility of substitutional Mn in a ZnO lattice is very low, which is less than 0.4%. Mn ions first dissolve into the substitutional sites in the ZnO lattice, thereby forming Mn2＋O4 tetrahedral coordination when x ≤ 0.001, then entering into the interstitial sites and forming Mn3＋O6 octahedral coordination when x ≥ 0.005. All the samples exhibit paramagnetic behaviors at room temperature, and antiferromagnetic coupling can be observed below 100 K.
基金
Project supported by the National Basic Research Program of China (Grant No.013CB934001)
the National Natural Science Foundation of China (Grant No.51272015)