A new process was designed to modify the hydroxy capped aliphatic hyperbranched polyester, derived from 2,2 bis(methylol) propionic acid and trimethylopropane in which the crude polyester reacted directly with maleic anhydride in bulk to transfer the hydroxy end groups to 4 carboxy 2 butante end groups. The modified polyester was characterized by IR, 1H NMR, DSC and viscosity measurement. The results indicated that no side reaction took place during the modifying step and the conversion for the reaction was calculated to be 88.9% based on the \+1H NMR spectra. The T g value shifted from 320 3 K for the crude polymer to 288 4 K for the modified polymer. Moreover, the UV curing coating of the midified polyester showed high performances in hardness, adhensive and water resistance. [WT5HZ]
A new process was designed to modify the hydroxy capped aliphatic hyperbranched polyester, derived from 2,2 bis(methylol) propionic acid and trimethylopropane in which the crude polyester reacted directly with maleic anhydride in bulk to transfer the hydroxy end groups to 4 carboxy 2 butante end groups. The modified polyester was characterized by IR, 1H NMR, DSC and viscosity measurement. The results indicated that no side reaction took place during the modifying step and the conversion for the reaction was calculated to be 88.9% based on the \+1H NMR spectra. The T g value shifted from 320 3 K for the crude polymer to 288 4 K for the modified polymer. Moreover, the UV curing coating of the midified polyester showed high performances in hardness, adhensive and water resistance. [WT5HZ]
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2000年第12期1950-1952,共3页
Chemical Journal of Chinese Universities
关键词
超支化聚合物
脂肪型聚酯
端基改性
Hyperbranched polymer
Aliphatic polyester
End groups
Modification