对ROAl2O3P2O5 系统玻璃中某些组分进行了去离子水及模拟生理液的耐蚀性测定.实验表明,ROAl2O3P2O5 在模拟生理液中的侵蚀规律异于通常的Na2OCaOSiO2P2O5 生物玻璃.试样的红外光谱验证了在该玻璃中兼有PO3 和P2O7 基团,具有稳定的Al(PO3)结构单元.
Chemical durability of selected compositions in RO Al 2O 3 P 2O 5(RAP) glass system(R=Zn,Mg) in deionic water and simulated physiologic solution were measured respectively. The measurements showed that the corrosion mechanism of RAP glass is quite different from that of Na 2O CaO SiO 2 P 2O 5 bioglass.The results from infrared spectrum experiments have confirmed the existence of PO 3 and P 2O 7 groups,as well as the stable Al(PO 3) group in the structure of RAP glass.