试验研究增塑剂品种和用量、硫化时间以及粘合体系对氢化丁腈橡胶(HNBR)粘合性能的影响。结果表明,当增塑剂D810用量为8份,硫化时间为35 min,采用粘合剂A-粘合剂RS-白炭黑粘合体系时,HNBR硫化胶的粘合性能最佳,综合物理性能较好。
The effects of the type and addition level of plasticizer,curing time and adhesion system on the adhesion of HNBR were experimentally investigated.The results showed that,when the addition level of plasticizer D810 was 8 phr,the curing time was 35 min,the adhesion system combining adhesive A,adhesive RS and silica was applied,the adhesion of HNBR vulcanizate was the best,and the comprehensive properties were excellent.