摘要
分析了铸轧3003铝合金坯料及均匀化退火前后的微观组织。在成品退火阶段,对各退火温度下的显微组织和力学性能进行检测,研究了均匀化退火对成品退火时组织和性能的影响。
The microstructure of roll casting 3003 aluminum alloy was observed pre and post homogenizing annealing. In final annealing,microstructure and mechanical property of samples at different annealing temperatures were analyzed. Effect of homogenizing treatment on micrestructure and mechanical property in final annealing was studied.