Using high aluminum refractory material as substrate at 1400℃, we studied the connections between several oxides such as Fe203, MnOv CuO, and the formation of defects such as coating crack, exfoliation, blistering, erosion, and fading away appeared in the application of high temperature infrared radiation coating. Analyses showed that thermal stress formed during the heating process due to the thermal expansion coefficient differential between the coating and the substrate, and volume effect caused by the crystal transferred when the temperature changed, which resulted in the coating crack and exfoliation. The gas produced by the reactions between components and binder or the components themselves during the heating process caused the coating blistering. The EMPA and XRD analyses show that oxides with low melting point in the penetrating area of the substrate may form eutectic with low melting point and produced thermal defects, which leads to the erosion by penetrating to the substrate. The valent changes of Fe2O3 and MnO2 during the heating process cause the volatilization of the oxides or the pulverization of the coatings, resulting in the coating fades away easily at high temperature for a long time.
Using high aluminum refractory material as substrate at 1400℃, we studied the connections between several oxides such as Fe203, MnOv CuO, and the formation of defects such as coating crack, exfoliation, blistering, erosion, and fading away appeared in the application of high temperature infrared radiation coating. Analyses showed that thermal stress formed during the heating process due to the thermal expansion coefficient differential between the coating and the substrate, and volume effect caused by the crystal transferred when the temperature changed, which resulted in the coating crack and exfoliation. The gas produced by the reactions between components and binder or the components themselves during the heating process caused the coating blistering. The EMPA and XRD analyses show that oxides with low melting point in the penetrating area of the substrate may form eutectic with low melting point and produced thermal defects, which leads to the erosion by penetrating to the substrate. The valent changes of Fe2O3 and MnO2 during the heating process cause the volatilization of the oxides or the pulverization of the coatings, resulting in the coating fades away easily at high temperature for a long time.
基金
Funded by the National Natural Science Foundation of China(Nos.51272195 and 51202175)
the Research Funds for the Central Universities(2012-Ia-012,2012-IV-105,2013-ZD-4)