Polyamide I1 （PAll） and its nanocomposites with different organoclay loadings were prepared by melt-compounding and subsequent pelletizing. The crystal phase transitions of PAl 1 and its clay nanocomposites were investigated by variable-temperature X-ray diffraction. It was found that the Brill transition of the nanocomposite was 20 K higher than that of the neat PAl 1 for both heating and cooling processes. The PAl 1 d-spacings of the nanocomposites were observed to be smaller than those of the neat PAl 1 for melt crystallization. The constraints imposed by the addition of layered clay, restricting the thermal expansion of the polymer chains, are probably responsible for such a reduction of the d-spacing.
Polyamide I1 （PAll） and its nanocomposites with different organoclay loadings were prepared by melt-compounding and subsequent pelletizing. The crystal phase transitions of PAl 1 and its clay nanocomposites were investigated by variable-temperature X-ray diffraction. It was found that the Brill transition of the nanocomposite was 20 K higher than that of the neat PAl 1 for both heating and cooling processes. The PAl 1 d-spacings of the nanocomposites were observed to be smaller than those of the neat PAl 1 for melt crystallization. The constraints imposed by the addition of layered clay, restricting the thermal expansion of the polymer chains, are probably responsible for such a reduction of the d-spacing.
基金
financially supported by the National Natural Science Foundation of China(No.51125011)
Guangxi Small Highland Innovation Team of Talents in Colleges and Universities
Guangxi Funds for Specially-appointed Expert