摘要
Kbphillipsite was prepared using a hydrothermal method. Soluble glass and sodium aluminate were used as raw materials in the absence of an organic template. Investigations regarding the K＋ ions were con- ducted at room temperature to determine the ion-exchange capacity in the seawater sample and the selectivity coefficient of the mixed K＋-Na~ solution. The sample was characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy dispersion spectroscopy （EDS）. The K＋ ion- exchange capacity is 51 mg/g in seawater and the selectivity coefficient is 75.1 in the mixed K＋-Na＋ solution. The sample has a selectivity preference for K＋, and therefore can be used to selectively extract potassium from seawater. The sample composed of Si, Al, K, Na, and O exhibits a cross-like shape and is a typical K-phillipsite structure.
Kbphillipsite was prepared using a hydrothermal method. Soluble glass and sodium aluminate were used as raw materials in the absence of an organic template. Investigations regarding the K＋ ions were con- ducted at room temperature to determine the ion-exchange capacity in the seawater sample and the selectivity coefficient of the mixed K＋-Na~ solution. The sample was characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy dispersion spectroscopy （EDS）. The K＋ ion- exchange capacity is 51 mg/g in seawater and the selectivity coefficient is 75.1 in the mixed K＋-Na＋ solution. The sample has a selectivity preference for K＋, and therefore can be used to selectively extract potassium from seawater. The sample composed of Si, Al, K, Na, and O exhibits a cross-like shape and is a typical K-phillipsite structure.
基金
the Natural Science Foundation of Shandong Province(ZR2010BQ024)
the Specialized Research Fund for the Doctoral Program of Higher Education(20100132120004)
the Fundamental Research Funds for the Central Universities (201013013)for financial support