摘要
Bi-layered thermally grown oxide （TGO） layer plays a major role in the spallation of Y2O3 stabilized ZrO2 （YSZ） layer form the bond coat in the thermal barrier coating （TBC） systems during oxidation. On the other hand, bi-layered TGO formation and growth in the TBC systems with nanostructured YSZ have not been deeply investigated during cyclic oxidation. Hence, Inconel 738/NiCrAlY/normal YSZ and Inconel 738/NiCrAlY/nano YSZ systems were pre-oxidized at 1000 °C and then subjected to cyclic oxidation at 1150 °C. According to microstructural observations, nanostructured YSZ layer over the bond coat should have less mi-cro-cracks and pinholes, due to the compactness of the nanostructure and the presence of nano zones that resulted in lower O infiltration into the nanothermal barrier coating system, formation of thinner and nearly continuous mono-layered thermally grown oxide on the bond coat during pre-oxidation, lower spinels formation at the Al2O3/YSZ interface and finally, reduction of bi-layered thermally grown oxide thickness during cyclic oxidation. It was found that pre-heat treatment and particularly coating microstructure could influence microstructural evolution （bi-layered TGO thickness） and durability of thermal barrier coating systems during cyclic oxidation.
Bi-layered thermally grown oxide （TGO） layer plays a major role in the spallation of Y2O3 stabilized ZrO2 （YSZ） layer form the bond coat in the thermal barrier coating （TBC） systems during oxidation. On the other hand, bi-layered TGO formation and growth in the TBC systems with nanostructured YSZ have not been deeply investigated during cyclic oxidation. Hence, Inconel 738/NiCrAlY/normal YSZ and Inconel 738/NiCrAlY/nano YSZ systems were pre-oxidized at 1000 °C and then subjected to cyclic oxidation at 1150 °C. According to microstructural observations, nanostructured YSZ layer over the bond coat should have less mi-cro-cracks and pinholes, due to the compactness of the nanostructure and the presence of nano zones that resulted in lower O infiltration into the nanothermal barrier coating system, formation of thinner and nearly continuous mono-layered thermally grown oxide on the bond coat during pre-oxidation, lower spinels formation at the Al2O3/YSZ interface and finally, reduction of bi-layered thermally grown oxide thickness during cyclic oxidation. It was found that pre-heat treatment and particularly coating microstructure could influence microstructural evolution （bi-layered TGO thickness） and durability of thermal barrier coating systems during cyclic oxidation.
基金
Project supported by the Ministry of Higher Education of Malaysia and Research Management Center of UTM(Post-Doctoral part)