摘要
制备了异烟酸氮氧化物(简计为HINO)/磷钼酸镍有机-无机络合物({[-Ni(H2O)8][H(H2O)2.5](HINO)4(PMo12O40)}n;简计为1)掺杂硅胶复合物(简计为1-SG1);采用红外光谱仪和X射线衍射仪证实了合成产物的结构.结果表明,化合物1的结构特征在1-SG1硅胶复合物中得以保留.与此同时,在约98%的相对湿度下,1-SG1在温度55~100℃范围内显示良好的导电性,其质子导电率达到8.98×10^-3~1.03×10^-2·cm^-1;并且,在同等条件下,1-SG1的质子导电性优于化合物1.
A silica gel composite (denoted as 1-SG1) doped with {[-Ni(H2O)8][H(H2O)2.5](HINO)4(PMo12O40)}n (1), a proton-conductive organic/inorganic complex of isonicotinic acid N-oxide (denoted as HINO) and nickel phosphomolybdate, was prepared by sol-gel method. The structure of as-synthesized 1-SG1 was confirmed by infrared spectrometry and X-ray diffraction, and its electric conductivity was calculated based on electrochemical impedance spectroscopic measurement. It was found that the structural characteristics of complex 1 are retained successfully in the silica gel skeleton of as-prepared 1-SG1 composite. Besides, 1-SG1 exhibits good proton conductivities of as much as 8.98×10-3~1.03×10-2·cm-1 in the tem- perature range of 55--100℃ under a relative humidity of 98% ; and in particular, it shows bet- ter proton conductivity than complex 1 at the same conditions, due to the presence of a large number of micropores and mesopores filled with "liquid".
出处
《化学研究》
CAS
2014年第1期63-66,71,共5页
Chemical Research
基金
National Natural Science Foundation of China(21171050)
关键词
异烟酸氮氧化物
磷钼酸镍
络合物
硅胶
复合材料
制备
质子导电性
isonicotinic acid N-oxide
nickel phosphomolybdate
complex
silica gel
composite
preparation
proton conductivity