： The superfine CaCO3 powder coated with SiO2 was synthesized. Through XRD technique, the cell parameters and crystallite size of reference and coated CaCO3 were calculated. SiO2 present in the state of amorphous and prevent the agglomeration and growth of CaCO3 micro-crystal. By comparing the result of XPS analysis of reference compound to coated sample, CaCO3 has been coated successfully with SiO2. The thickness of the coating is about 2.4～ 3.4nm. From the difference(0.8eV increase) of the binding energy of Ca2p, we presume that the bind Si-O-Ca has formed in the surface of CaCO3.
： The superfine CaCO3 powder coated with SiO2 was synthesized. Through XRD technique, the cell parameters and crystallite size of reference and coated CaCO3 were calculated. SiO2 present in the state of amorphous and prevent the agglomeration and growth of CaCO3 micro-crystal. By comparing the result of XPS analysis of reference compound to coated sample, CaCO3 has been coated successfully with SiO2. The thickness of the coating is about 2.4～ 3.4nm. From the difference(0.8eV increase) of the binding energy of Ca2p, we presume that the bind Si-O-Ca has formed in the surface of CaCO3.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2001年第1期134-138,共5页
Chinese Journal of Inorganic Chemistry