摘要
The microstructure evolution and mechanical properties of a ZK60 magnesium alloy produced by the semi-solid thermal transformation （SSTT） route and the recrystallization and partial melting （RAP） route were studied, respectively. The microstructure evolution during partial remelting was studied at different temperatures for different time. The tensile mechanical properties of thixoformed components by the two routes at room temperature were examined. The results show that coalescence is dominant in the SSTT alloy and Ostwald ripening is dominant in the RAP alloy. Compared with the SSTT route, the RAP route can produce finer semi-solid microstructure under the similar isothermal holding condition. The microstructure of the RAP alloy is much more spheroidized compared with the SSTT alloy. Thixoforming for the ZK60 magnesium alloy produced by the SSTT and RAP route results in successful filling of the die, and the thixoforming process improves the mechanical properties of ZK60 magnesium alloy. The RAP alloy shows significantly advantageous mechanical properties over that of the SSTT alloy.
研究了分别由半固态热成形方法(SSTT)和部分重熔再结晶方法(RAP)得到的ZK60镁合金在一定温度下显微组织随等温时间的变化和触变成形试样的力学性能。结果表明,合并长大机制在SSTT合金的组织变化中占主导地位,熟化机制在RAP合金的组织变化中起主要作用。在相同的等温条件下,与SSTT方法相比,RAP方法可以得到更细小的半固态显微组织,RAP合金组织比SSTT合金组织更圆整。由SSTT方法和RAP方法得到的ZK60镁合金触变成形后均得到了较理想的成形件,触变成形工艺提高了材料的力学性能。与SSTT合金相比,RAP合金具有更优越的力学性能。