摘要
Mid-infrared（MIR） emissions of 2.4 and 3.5 μm from Tm3＋：LiYF4 single crystals attributed to3H4 →3H5 and3H5 →3F4 transitions as well as MIR emissions of 4.2,4.3,and 4.5 μm from Nd3＋：LiYF4 lasers attributed to4I15/2 →4I13/2,4I13/2 →4I11/2,and4I11/2 →4I9/2 transitions,respectively,are observed.LiYF4 single crystals possess high transmittance of over 85% in the 2.5-6 μm range.The large emission crosssections of Tm-doped crystals at 2.4 μm（1.9×10-20cm2） and Nd-doped crystals at 4.2 μm（0.84×10-20 cm2） as well as the high rare-earth doping concentrations,excellent optical transmission,and chemicalphysical properties of the resultant samples indicate that Nd3＋and Tm3＋singly doped crystals may be promising materials for application in MIR lasers.
Mid-infrared（MIR） emissions of 2.4 and 3.5 μm from Tm3＋：LiYF4 single crystals attributed to3H4 →3H5 and3H5 →3F4 transitions as well as MIR emissions of 4.2,4.3,and 4.5 μm from Nd3＋：LiYF4 lasers attributed to4I15/2 →4I13/2,4I13/2 →4I11/2,and4I11/2 →4I9/2 transitions,respectively,are observed.LiYF4 single crystals possess high transmittance of over 85% in the 2.5-6 μm range.The large emission crosssections of Tm-doped crystals at 2.4 μm（1.9×10-20cm2） and Nd-doped crystals at 4.2 μm（0.84×10-20 cm2） as well as the high rare-earth doping concentrations,excellent optical transmission,and chemicalphysical properties of the resultant samples indicate that Nd3＋and Tm3＋singly doped crystals may be promising materials for application in MIR lasers.
基金
supported by the National Natural Science Foundation of China(Nos.51272109 and 50972061)
the Natural Science Foundation of Zhejiang Province(No.R4100364)
the Natural Science Foundation of Ningbo City(No.2012A610115)
the K.C.Wong Magna Fund in Ningbo University