摘要
通过断裂实验、二维有限元分析(2-D FEA)、三维有限元分析(3-D)以及EPRI解等4种方法获得了工业纯钛(CP Ti)紧凑拉伸试验(CT)的J积分。结果表明,EPRI解获得的J积分与2-D FEA结果吻合,但是它们明显低于实验结果,而3-D FEA获得的J积分更接近于实验值。为了提高J积分的估算精度,提出了基于3-D FEA改进的EPRI解,并用实验结果进行了验证。此外,将由原EPRI解和改进的EPRI解获得的J积分建立的CP Ti失效评定曲线(FAC)与实验结果进行比较,发现EPRI解的改进不仅提高了J积分的估算精度,而且提高了FAC的可靠性。
In this paper, the J-integral of commerciaUy pure titanium (CP Ti) for standard compact tensile (CT) specimen was obtained by four methods containing fracture experiment, two-dimensional (2-D) finite element analysis (FEA), three-dimensional (3-D) FEA, and the calculation formula in electric power research institute (EPRI). Although the J-integral obtained by EPRI solution is consistent with that by 2-D FEA, they are lower than the result of the experiment. Moreover, the J-integral obtained by 3-D FEA is more close to that of the experiment. In order to improve the prediction accuracy of J-integral by EPRI solution, the improved EPRI solution was developed based on 3-D FEA and verified by the experiment. In addition, two failure assessment curves (FACs) ofCP Ti correspond- ing to traditional EPRI solution and the improved one were compared with the experimental results, which indicates that the improved EPRI solution not only improve the prediction accuracy of J-integral, but also increases the reliability of FAC.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2014年第2期257-263,共7页
Rare Metal Materials and Engineering
基金
National Natural Science Foundation of China(51075199)
Graduate Student Scientific Innovative Project of Jiangsu Province(CXZZ11_0341)