Calcium tungstate phosphors activated by the Ln3＋ ions （Ln-Pr, Nd, Tb, Yb） were synthesized by a traditional high-temperature solid-state method. The crystal structures and morphologies of the products were characterized by scanning electron microscopy （SEM）, X-ray powders diffraction （XRD） and infrared spectra （FT-1R）. The samples were fotmd to show luminescence properties （down-conversion, DC, at excitation wavelength 254 nm and up-conversion, UC, at excitation wavelength 980 nm）. CaWO4 doped with Tb3＋/yb3＋ showed green DC and UC luminescence characteristic of Tb（Ⅲ） ion in the range of 470-660 nm, cor- responding to the 5D4→7F6,5,4,3,2 electronic transition. CaWO4 doped with Pr3＋/Yb3＋ showed week blue, green and red （DC and UC） luminescence of Pr（Ⅲ） ion, in the wavelength region of 450-700 nm. Emission peaks were ascribed to the 3P1→3H4,5,6, 3P0→3H4,5,6, 3P1→3F2 and 3P0→3F2 transitions, respectively. CaWO4 doped with Nd3＋/yb3＋ phosphor emitted orange UC luminescence at 450-690 nm （2p3/2→4I15/2, 4G7/2→419/2,11/2,13/2） and strong near-infrared UC luminescence at 720-900 nm （4F7/2＋4S3/2→4419/2, 4F5/2＋2H3/2→419/2, 4F3/2→4I9/2） which is the characteristic of Nd（Ⅲ） ion.
Calcium tungstate phosphors activated by the Ln3＋ ions （Ln-Pr, Nd, Tb, Yb） were synthesized by a traditional high-temperature solid-state method. The crystal structures and morphologies of the products were characterized by scanning electron microscopy （SEM）, X-ray powders diffraction （XRD） and infrared spectra （FT-1R）. The samples were fotmd to show luminescence properties （down-conversion, DC, at excitation wavelength 254 nm and up-conversion, UC, at excitation wavelength 980 nm）. CaWO4 doped with Tb3＋/yb3＋ showed green DC and UC luminescence characteristic of Tb（Ⅲ） ion in the range of 470-660 nm, cor- responding to the 5D4→7F6,5,4,3,2 electronic transition. CaWO4 doped with Pr3＋/Yb3＋ showed week blue, green and red （DC and UC） luminescence of Pr（Ⅲ） ion, in the wavelength region of 450-700 nm. Emission peaks were ascribed to the 3P1→3H4,5,6, 3P0→3H4,5,6, 3P1→3F2 and 3P0→3F2 transitions, respectively. CaWO4 doped with Nd3＋/yb3＋ phosphor emitted orange UC luminescence at 450-690 nm （2p3/2→4I15/2, 4G7/2→419/2,11/2,13/2） and strong near-infrared UC luminescence at 720-900 nm （4F7/2＋4S3/2→4419/2, 4F5/2＋2H3/2→419/2, 4F3/2→4I9/2） which is the characteristic of Nd（Ⅲ） ion.