Broadband waveguiding through light-emitting strips directly written in a blank lithium fluoride crystal with a femtosecond laser is reported. Light guiding was observed at several optical wavelengths, from blue, 458 nm, to near-infrared, at 155nm. Visible photoluminescence spectra of the optically active F2 and F33 color centers produced by the fs laser writing process were measured. The wavelength-dependent refractive index increase was estimated to be in the order of 10-3-10-4 in the visible and near-infrared spectral intervals, which is consistent with the stable formation of point defects in LiF.
Broadband waveguiding through light-emitting strips directly written in a blank lithium fluoride crystal with a femtosecond laser is reported. Light guiding was observed at several optical wavelengths, from blue, 458 nm, to near-infrared, at 155nm. Visible photoluminescence spectra of the optically active F2 and F33 color centers produced by the fs laser writing process were measured. The wavelength-dependent refractive index increase was estimated to be in the order of 10-3-10-4 in the visible and near-infrared spectral intervals, which is consistent with the stable formation of point defects in LiF.