In the present work,hierarchical nanostructured titanium dioxide(TiO2) films were fabricated on Ti-25Nb-3Mo-2Sn-3Zr(TLM) alloy for biomedical applications via one-step anodization process in ethylene glycolbased electrolyte containing 0.5wt% NH4F.The nanostructured TiO2 films exhibited three distinct types depending on the anodization time:top irregular nanopores(INP)/beneath regular nanopores(RNP),top INP/middle regular nanotubes(RNT)/bottom RNP and top RNT with underlying RNP.The evolution of the nanostructured TiO2 films with anodization time demonstrated that self-organizing nanopores formed at the very beginning and individual nanotubes originated from underlying nanopore dissolution.Furthermore,a modified two-stage self-organizing mechanism was introduced to illustrate the growth of the nanostructured TiO2 films.Compared with TLM titanium alloy matrix,the TiO2 films with special nano-structure hold better hydrophilicity and higher specific surface area,which lays the foundation for their biomedical applications.
In the present work,hierarchical nanostructured titanium dioxide（TiO2） films were fabricated on Ti-25Nb-3Mo-2Sn-3Zr（TLM） alloy for biomedical applications via one-step anodization process in ethylene glycolbased electrolyte containing 0.5wt% NH4F.The nanostructured TiO2 films exhibited three distinct types depending on the anodization time：top irregular nanopores（INP）/beneath regular nanopores（RNP）,top INP/middle regular nanotubes（RNT）/bottom RNP and top RNT with underlying RNP.The evolution of the nanostructured TiO2 films with anodization time demonstrated that self-organizing nanopores formed at the very beginning and individual nanotubes originated from underlying nanopore dissolution.Furthermore,a modified two-stage self-organizing mechanism was introduced to illustrate the growth of the nanostructured TiO2 films.Compared with TLM titanium alloy matrix,the TiO2 films with special nano-structure hold better hydrophilicity and higher specific surface area,which lays the foundation for their biomedical applications.
基金
Supported by the National Natural Science Foundation of China(No.51372169)
Natural Science Foundation of Tianjin(No.11JCZDJC17300)