摘要
An efficient approach was introduced for improving the condition of major controlled rolling process pa- rameters of roughing, finishing and coiling temperatures and optimizing these parameters to obtain minimum grain size and maximum dome height simultaneously. Taguchi method combined with grey relational analysis was applied to achieve optimum grain size and dome height during controlled rolling process. For this purpose, four levels for the above temperatures were chosen and sixteen experiments were conducted based on orthogonal array of Taguchi meth- od. Based on Taguchi approach, signal-to-noise （S/N） ratios were calculated and used in order to obtain the opti- mum levels for every input parameter. Analysis of variance revealed that finishing and coiling temperatures have the maximum effect on the grain size and dome height of microalloyed steels. The confirmation tests with the optimal levels of parameters indicated that the grain size and dome height of controlled rolled microalloyed steels can be im- proved effectively through this approach.
An efficient approach was introduced for improving the condition of major controlled rolling process pa- rameters of roughing, finishing and coiling temperatures and optimizing these parameters to obtain minimum grain size and maximum dome height simultaneously. Taguchi method combined with grey relational analysis was applied to achieve optimum grain size and dome height during controlled rolling process. For this purpose, four levels for the above temperatures were chosen and sixteen experiments were conducted based on orthogonal array of Taguchi meth- od. Based on Taguchi approach, signal-to-noise （S/N） ratios were calculated and used in order to obtain the opti- mum levels for every input parameter. Analysis of variance revealed that finishing and coiling temperatures have the maximum effect on the grain size and dome height of microalloyed steels. The confirmation tests with the optimal levels of parameters indicated that the grain size and dome height of controlled rolled microalloyed steels can be im- proved effectively through this approach.