Microstructure and Mechanical Properties of Gear Steels After High Temperature Carburization 被引量:10

Microstructure and Mechanical Properties of Gear Steels After High Temperature Carburization
原文传递
导出
摘要 High temperature carburization is becoming more and more attractive because it can remarkably reduce processing time and increase productivity. However, the commonly used gear steels which are microalloyed by Al are not suitable for high temperature carburization due to abnormal grain coarsening. The gear steel 20CrMnTiNb, which is microalloyed with 0. 048% Nb and 0. 038% Ti, has been compared with the gear steel 20CrMn in terms of microstructure in the case of hardened layer and in the core after carburizing at 1000 ℃ for 4 h and mechanical prop- erties after carburizing and pseudo-carburizing. The results indicate that the fine austenite grains exist in the carbu- rized case of 20CrMnTiNb steel, while there is abnormal coarsening and duplex grain structure in the case and core of steel 20CrMn. The average prior austenite grain sizes are 19.5 and 34.2 μm for the steels 20CrMnTiNb and 20CrMn, respectively. In addition, the mechanical properties of 20CrMnTiNb steel are superior to those of 20CrMn steel. In particular, the HV hardness of the former is higher than that of the latter by about 40--70 in the range of less than 0. 7 mm in depth. Therefore, the steel 20CrMnTiNb is suitable for high temperature carburization. High temperature carburization is becoming more and more attractive because it can remarkably reduce processing time and increase productivity. However, the commonly used gear steels which are microalloyed by Al are not suitable for high temperature carburization due to abnormal grain coarsening. The gear steel 20CrMnTiNb, which is microalloyed with 0. 048% Nb and 0. 038% Ti, has been compared with the gear steel 20CrMn in terms of microstructure in the case of hardened layer and in the core after carburizing at 1000 ℃ for 4 h and mechanical prop- erties after carburizing and pseudo-carburizing. The results indicate that the fine austenite grains exist in the carbu- rized case of 20CrMnTiNb steel, while there is abnormal coarsening and duplex grain structure in the case and core of steel 20CrMn. The average prior austenite grain sizes are 19.5 and 34.2 μm for the steels 20CrMnTiNb and 20CrMn, respectively. In addition, the mechanical properties of 20CrMnTiNb steel are superior to those of 20CrMn steel. In particular, the HV hardness of the former is higher than that of the latter by about 40--70 in the range of less than 0. 7 mm in depth. Therefore, the steel 20CrMnTiNb is suitable for high temperature carburization.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2013年第12期140-145,共6页
基金 Item Sponsored by National High Technology Research and Development Program(863)of China(2006AA03Z526)
关键词 gear steel high temperature carburization austenite grain size effective case depth gear steel high temperature carburization austenite grain size effective case depth
  • 相关文献

参考文献4

二级参考文献39

  • 1Goldstein J I,Moren A E. Diffusion Modeling of the Carburization Process [J]. Metall Trans, 1978, A, 9 : 1515.
  • 2Heat Treating, ASM Metals Handbook [M]. ASM International, 1991.
  • 3Harris F E. Cae Depth-An Attempt at a Practical Definition [J]. Metal Progress,1943,44(2) :265.
  • 4Wise J P, Matlock D K. SAE Technical Paper Series [R]. No. 200-01-0611, SAE, PA: Warrendale,2000.
  • 5Cornelissen B E, Matlock D K, Krauss G, et al. SAE Technical Paper No. 1999-01-0602, SAE, PA: Warrendale,1999.
  • 6Pacheco J L, Krauss G. Carburizing: Processing and Performance [M]. OH: Am Soc Met Metals Park,1989.
  • 7Kaori Miyata, Tomohiro Omura, Takahiro Kushida, et al. Coarsening Kinetics of Multicomponent MC-Type Carbides in High-Strength Low-Alloy Steels [J]. Metallurgical and Materials Transactions, 2003,34A : 1565.
  • 8Narita K. Physical Chemistry of the Groups Ⅳa(Ti,Zr) ,Ⅴa (V,Nb,Ta) and the Rare Earth Elements in Steel [J]. Trans Iron Steel Inst Jpn, 1978,18 ; 145.
  • 9Goldstein J I, Moren A E. Diffusion modeling of the carburization process[J]. Metall Trans A, 1978, 9:1515 - 1525.
  • 10住田庸,野村一衛.浸炭処理される驅動系鍛造部品の動向と課題[J].熱処理,2005,45(2):76-79.

共引文献66

同被引文献98

引证文献10

二级引证文献52

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部