Preparing SnO2 with hierarchical micro/nano structures by hydrothermal, coordination, templating and electrochemical deposition methods and their mechanisms are investigated. The result shows that the echinus-like SnO2 prepared by Method 1 is a typical Ostwald mechanism that develops from internally to externally. The cabbage-like SnO2 by Method 2 is produced with oxalic acid as complexing agent to set-up precursor of SnO2, and then precursors are bocked around the body that is around the body being bocked. The nest-like SnO2 by Method 3 is controlled by citric acid as coordinator for the nucleation as well as the grow rate and setup process. Spongy-like SnO2 by Method 4 is produced using PST as template, PST is be infiltered into SnO2 precursor by gravity and capillary and treated thermally to form a multiporous structure. The petal-like SnO2 by Method 5 is formed with crystal deposition emergence due to oxidation-reduction reactions of two electrodes in an electric field. XRD analyses shows that the five results are all pure phase SnO2. It provides basic data for SnOE industrial application.
Preparing SnO2 with hierarchical micro/nano structures by hydrothermal, coordination, templating and electrochemical deposition methods and their mechanisms are investigated. The result shows that the echinus-like SnO2 prepared by Method 1 is a typical Ostwald mechanism that develops from internally to externally. The cabbage-like SnO2 by Method 2 is produced with oxalic acid as complexing agent to set-up precursor of SnO2, and then precursors are bocked around the body that is around the body being bocked. The nest-like SnO2 by Method 3 is controlled by citric acid as coordinator for the nucleation as well as the grow rate and setup process. Spongy-like SnO2 by Method 4 is produced using PST as template, PST is be infiltered into SnO2 precursor by gravity and capillary and treated thermally to form a multiporous structure. The petal-like SnO2 by Method 5 is formed with crystal deposition emergence due to oxidation-reduction reactions of two electrodes in an electric field. XRD analyses shows that the five results are all pure phase SnO2. It provides basic data for SnOE industrial application.
基金
Supported by fund of the Excellent Science&Technology Innovate Team Program for Young and Middle-aged Talents in University of Hubei Province(T201225)
Hubei Provincial Key Laboratory of Plant Anti-Cancer Active Substance Purification and Application,The Second Excellent Teacher Team of Hubei University of Education(2012K203)