Both terminated functional isotactic polypropylene （iPP） and block copolymers containing iPP segment are desirable for commercial applications. This paper provides a convenient, highly-efficient method to prepare hydroxyl-terminated isotactic polypropylene （iPP-t-OH） and functional di-block copolymer containing the iPP segment through a combination of coordination polymerization and coupling reaction. The coordination polymerization was catalyzed by TiCI4/MgCI2/AIEt3 catalyst system using ZnEt2 as chain transfer agent. Further, the Zn-terminated iPP was oxidized and subsequently hydrolyzed to provide iPP-t-OH. Soxhlet extraction and 13C NMR were used to calculate the isotacticity of iPP-t-OH. The degree of polymerization and the number of hydroxyl groups at the chain end of iPP-t-OH were measured by GPC and 1H NMR. Despite the high molecular weight and heterogeneous reaction, iPP-t-OH is effectively linked with PEG-t-NCO to produce di-block copolymers. DSC analysis of the di-block copolymer shows an obvious decrease in Tm and To, which indicated that PEG was successfully linked to the terminal end of iPP.
Both terminated functional isotactic polypropylene （iPP） and block copolymers containing iPP segment are desirable for commercial applications. This paper provides a convenient, highly-efficient method to prepare hydroxyl-terminated isotactic polypropylene （iPP-t-OH） and functional di-block copolymer containing the iPP segment through a combination of coordination polymerization and coupling reaction. The coordination polymerization was catalyzed by TiCI4/MgCI2/AIEt3 catalyst system using ZnEt2 as chain transfer agent. Further, the Zn-terminated iPP was oxidized and subsequently hydrolyzed to provide iPP-t-OH. Soxhlet extraction and 13C NMR were used to calculate the isotacticity of iPP-t-OH. The degree of polymerization and the number of hydroxyl groups at the chain end of iPP-t-OH were measured by GPC and 1H NMR. Despite the high molecular weight and heterogeneous reaction, iPP-t-OH is effectively linked with PEG-t-NCO to produce di-block copolymers. DSC analysis of the di-block copolymer shows an obvious decrease in Tm and To, which indicated that PEG was successfully linked to the terminal end of iPP.
基金
supported by the National Natural Science Foundation of China(No.51173157)
National High-Tech R&D Program of China(No.2012AA040305)
the Major State Basic Research Programs(No.2011CB606001)