Cerium-doped Sr3（A11-x,Six）O4-xNxF oxynitride phosphors with different x values were synthesized by solid-state reaction. The structure and optical properties of these phosphors were investigated by X-ray diffraction （XRD）, energy dispersive spectroscopy （EDS） and photoluminescence （PL） spectra. The XRD results showed that SiN substitution for Al-O） did not change the structure of Sr3A104F host and there was no impurity for x〈0.6. With the increasing ofx values, the absorption of phosphors at the blue region was enhanced and the emitting band varied from 519 to 529 nm under the 460 nm blue light excitation. The red shift of the emission band was associated with an increase in the crystal-field splitting and the covalence, which arose from the incorporation of N. More- over, the incorporation of N also improved the thermal quenching properties and the external quantum efficiency with a maximum value up to 43.3%, indicating that this phosphor is a promising candidate for white LEDs application.
Cerium-doped Sr3（A11-x,Six）O4-xNxF oxynitride phosphors with different x values were synthesized by solid-state reaction. The structure and optical properties of these phosphors were investigated by X-ray diffraction （XRD）, energy dispersive spectroscopy （EDS） and photoluminescence （PL） spectra. The XRD results showed that SiN substitution for Al-O） did not change the structure of Sr3A104F host and there was no impurity for x〈0.6. With the increasing ofx values, the absorption of phosphors at the blue region was enhanced and the emitting band varied from 519 to 529 nm under the 460 nm blue light excitation. The red shift of the emission band was associated with an increase in the crystal-field splitting and the covalence, which arose from the incorporation of N. More- over, the incorporation of N also improved the thermal quenching properties and the external quantum efficiency with a maximum value up to 43.3%, indicating that this phosphor is a promising candidate for white LEDs application.
基金
Porject supported by National Basic Research Program of China(973 program,2014CB643801)
National Natural Science Foundation of China(51102021
51302026)