Hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） for 2A14-T6 high strength aluminum alloy was carried out and the effects of variable polarity frequency with constant pulse current frequency 40 kHz on weld bead geometry, microstrueture and microhardness were analyzed. Experimental results indicate that, compared to that of the conventional VP-GTAW process, the weld depth and ratio of weld depth to width are improved significantly by the variable polarity frequency in the HPVP-GTAW process, which the ratio of weld depth to width is improved by 36% at equal variable polarity frequency of 100 Hz, and improved by 55% with that of 200 Hz. Weld microstructure and microhardness distribution are changed obviously with the increase of variable polarity frequency. In the conventional VP-GTA W process, the grains in weld central zone are coarser, and the microhardness in weld central zone and fusion zone is about 95 HV and the lowest 82 HV, respectively. The microhardness is enhanced to a certain extent both in the weld central zone and fusion zone with the variation of variable polarity frequency in the HPVP-GTAW process due to the refinement and uniformity of weld microstructure. With the variable polarity frequency of 600 Hz, the microhardness in weld central zone and fusion zone reaches nearly 110 HV and 97 HV, respectively.
Hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） for 2A14-T6 high strength aluminum alloy was carried out and the effects of variable polarity frequency with constant pulse current frequency 40 kHz on weld bead geometry, microstrueture and microhardness were analyzed. Experimental results indicate that, compared to that of the conventional VP-GTAW process, the weld depth and ratio of weld depth to width are improved significantly by the variable polarity frequency in the HPVP-GTAW process, which the ratio of weld depth to width is improved by 36% at equal variable polarity frequency of 100 Hz, and improved by 55% with that of 200 Hz. Weld microstructure and microhardness distribution are changed obviously with the increase of variable polarity frequency. In the conventional VP-GTA W process, the grains in weld central zone are coarser, and the microhardness in weld central zone and fusion zone is about 95 HV and the lowest 82 HV, respectively. The microhardness is enhanced to a certain extent both in the weld central zone and fusion zone with the variation of variable polarity frequency in the HPVP-GTAW process due to the refinement and uniformity of weld microstructure. With the variable polarity frequency of 600 Hz, the microhardness in weld central zone and fusion zone reaches nearly 110 HV and 97 HV, respectively.
基金
This work is supported by the National Natural Science Foundation of China （Grant No. 51005011 ） and the Fundamental Research Funds for the Central Universities （ YWF-12-LGJC-001 ）.