The magnetic measurements of the single crystal of Mn3 single-molecule magnet under high pressure at T=2 K have been performed.We find both the antiferromagnetic intermolecular coupling parameter J and the effective energy barrier to vary compared with the measurements at low pressure.The increase of|J|is estimated to be 12%at 0.7 GPa when compared with that of0 GPa,whereas the effective energy barrier becomes smaller with increasing pressure.Our results demonstrate that the intermolecular interaction of single-molecule magnet can be changed by pressure.Compared with the normal magnetic alloy,the effect of pressure on the magnetic properties of Mn3 is much more prominent,which implies that Mn3 may have great potential in magnetic multifunctional material.
The magnetic measurements of the single crystal of Mn3 single-molecule magnet under high pressure at T=2 K have been performed.We find both the antiferromagnetic intermolecular coupling parameter J and the effective energy barrier to vary compared with the measurements at low pressure.The increase of｜J｜is estimated to be 12%at 0.7 GPa when compared with that of0 GPa,whereas the effective energy barrier becomes smaller with increasing pressure.Our results demonstrate that the intermolecular interaction of single-molecule magnet can be changed by pressure.Compared with the normal magnetic alloy,the effect of pressure on the magnetic properties of Mn3 is much more prominent,which implies that Mn3 may have great potential in magnetic multifunctional material.
基金
supported by the National Key Basic Research Program of China(Grant No.2011CB921702)
the National Natural Science Foundation of China(Grant No.11104331)