The tetrapod ZnO nanostructures are synthesized on the Si （100） substrates using the chemical va- por deposition （CVD） method at 1000 ℃. Each nanostructure has four arms which are about 3-10 μm in length and 0.2-1.5 μm in diameter. Further analyses on structure demonstrate that the tetrapod ZnO nanostructures have single crystalline wurtzite hexagonal structure preferentially oriented in c-axis. The photoluminescence （PL） mea- surements of the tetrapod ZnO nanostructures revealed a UV peak at 382 nm corresponding to the free exciton emission, and a green peak at 523 nm arising from deep level emission. For comparative analysis, cathodolumines- cence （CL） spectra obtained from different regions of an individual tetrapod are investigated. Moreover, a possible growth mechanism of the tetrapod ZnO nanostructures is also discussed based on the experimental results.
The tetrapod ZnO nanostructures are synthesized on the Si （100） substrates using the chemical va- por deposition （CVD） method at 1000 ℃. Each nanostructure has four arms which are about 3-10 μm in length and 0.2-1.5 μm in diameter. Further analyses on structure demonstrate that the tetrapod ZnO nanostructures have single crystalline wurtzite hexagonal structure preferentially oriented in c-axis. The photoluminescence （PL） mea- surements of the tetrapod ZnO nanostructures revealed a UV peak at 382 nm corresponding to the free exciton emission, and a green peak at 523 nm arising from deep level emission. For comparative analysis, cathodolumines- cence （CL） spectra obtained from different regions of an individual tetrapod are investigated. Moreover, a possible growth mechanism of the tetrapod ZnO nanostructures is also discussed based on the experimental results.
基金
Project supported by the Fundamental Research Funds for the Central Universities(Nos.JUSRP11230,JUSRP51323B)
the Natural Science Foundation of Jiangsu Province(No.BK2012110)
the PAPD of Jiangsu Higher Education Institutions
the Summit of the Six TopTalents Program of Jiangsu Province(No.DZXX-053)