碳化硅超细粉的制备新法 被引量:7

New Method for Preparation of SiC Ultrafine Powders
下载PDF
导出
摘要 用一种新的方法———双重加热法制备了直径在 5 0~ 6 0nm范围内的SiC超细粉 ,用化学分析方法、X射线衍射、透射电子显微镜等手段对SiC超细粉进行了表征。研究结果表明 ,用双重加热法制备SiC超细粉的最佳温度为135 0℃ ,恒温时间为 6 0min ,SiC超细粉的产率可达 98% (质量分数 ) The SiC ultrafine powders,which diameter is in the range of 50~60nm,were prepared by a new method named double heating method.SiO 2 nanometer powder and carbon nanometer powder were used as starting materials.The character of the SiC ultrafine powders was determined by the chemical analysis methold,XRD and TEM.The experimental results show that the best temperature for preparing SiC ultrafine powders is 1350℃,and the time is 60min,the yield ratio of the SiC ultrafine powders is about 98%. The double heating method is a new method for prepared SiC ultrafine powders with a large amount and a low costing.
作者 戴长虹 水丽
出处 《中国粉体技术》 CAS 2001年第1期10-11,共2页 China Powder Science and Technology
关键词 碳化硅 超细粉 陶瓷材料 双重加热法 SiC ultrafine powder preparation
  • 相关文献

参考文献2

  • 1戴长虹.双重加热炉[P].CN 2318588.1999—05—12.
  • 2Chrysanthou A,Grieveson P.Formation of silicon carbide whiskers and theirmicrostructure[J].J Mater Sci,1991,26 :3463

共引文献3

同被引文献110

引证文献7

二级引证文献21

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部