以塞拉利昂高铝铁矿粉及其他5种烧结常用铁矿粉为原料,通过添加CaO、SiO2、Al2O3纯试剂改变铁矿粉中三种组分的含量,并分析了其对铁矿粉液相流动性的影响,比较了6类铁矿粉液相流动性对SiO2、Al2O3含量的敏感性差异,研究了混合矿粉液相流动性随塞拉利昂高铝铁矿粉配比的变化并进行了烧结试验。结果表明,随着CaO配比的增加,铁矿粉的液相流动性变好,其中塞拉利昂高铝铁矿粉变化的幅度最大;SiO2含量对塞拉利昂高铝铁矿粉液相流动性的影响较Al2O3含量更为明显;随着塞拉利昂高铝铁矿粉配比增加,混合矿粉的液相液动性指数降低,烧结矿的强度和成品率下降。
Using the Sierra Leone high alumina iron ore and 5 other iron ores as raw materials ,this pa-per analyzes the influence of adding pure reagents CaO ,SiO2 ,Al2 O3 on the fluidity of iron ores . Differences in fluidity with different proportions of CaO ,SiO2 and Al2 O3 as well as differences in sen-sibility to SiO2 and Al2 O3 contents are compared .Furthermore ,pot sintering experiments were con-ducted of the variation in fluidity of ore blending with increasing proportion of Sierra Leone high alu-mina iron ore .It is found that ,the fluidity of iron ore is influenced by CaO proportion ,the fluidity of iron ore is improved with increasing proportion of CaO with the variation of Sierra Leone high alumina iron ore being the maximum .It is also found that SiO2 content influences the fluidity of Sierra Leone high alumina iron ore more than Al2 O3 content ,the deterioration of fluidity of ore blending has harm-ful influence on sintering ,and favorable fluidity of ore blending is the basis of efficient solidification of sinter .
出处
《武汉科技大学学报》
CAS
2014年第2期86-90,共5页
Journal of Wuhan University of Science and Technology
基金
国家科技支撑计划资助项目(2011BAC01B02)