摘要
The solid solutions Ce 1- x Eu x O 2- δ ( x =0\^10—0\^50) were synthesized by high temperature and high pressure. The XRD measurement showed that the solid solution was crystallized in cubic fluorite type structure and the lattice parameter increased with the content of Eu increasing up to x =0.4. The solution limit was \%ca.\% 0.4 under the condition of 3.6 GPa, 840—1 020 ℃. The XPS data showed that the Eu ions are Eu 3+ and trace of Ce 4+ ions were reduced to Ce 3+ ions during synthesis of high temperature and high pressure. The ionic conduction for Ce 0.8 Eu 0.2 O 2- δ was measured by impedance spectroscopy and it was found that the activation energy was 1.07 eV and the conductivity was 3.43×10 -5 S·cm -1 at 550 ℃.
The solid solutions Ce 1- x Eu x O 2- δ ( x =0\^10—0\^50) were synthesized by high temperature and high pressure. The XRD measurement showed that the solid solution was crystallized in cubic fluorite type structure and the lattice parameter increased with the content of Eu increasing up to x =0.4. The solution limit was \%ca.\% 0.4 under the condition of 3.6 GPa, 840—1 020 ℃. The XPS data showed that the Eu ions are Eu 3+ and trace of Ce 4+ ions were reduced to Ce 3+ ions during synthesis of high temperature and high pressure. The ionic conduction for Ce 0.8 Eu 0.2 O 2- δ was measured by impedance spectroscopy and it was found that the activation energy was 1.07 eV and the conductivity was 3.43×10 -5 S·cm -1 at 550 ℃.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2001年第3期368-370,共3页
Chemical Journal of Chinese Universities
基金
国家自然科学基金 !(批准号 :1980 40 0 5 )
吉林大学无机合成与制备化学教育部重点实验室基金!资助