摘要
The Zn1-xCuxO polycrystalline materials were prepared by doping CuO into wurtzite ZnO through solid state reaction. The high concentration of copper doping in ZnO exhibited remarkable room temperature ferromagnetism. The Experiments showed that the magnetization saturation rose with the increase of Cu content. For the low Cu content sample, the hysteresis loop was slightly tilted which indicated that the diamagnetism coexisted in this sample. The temperature dependence of magnetization of Zn1-xCuxO revealed that the magnetic exchange coupling depended on the doping concentration of Cu and there were many different local environments for magnetism. The measured hysteresis loop and temperature dependence of magnetization were overall performance of the magnetism coming from a wide distribution of ferromagnetic exchange couplings.
The Zn1-xCuxO polycrystalline materials were prepared by doping CuO into wurtzite ZnO through solid state reaction. The high concentration of copper doping in ZnO exhibited remarkable room temperature ferromagnetism. The Experiments showed that the magnetization saturation rose with the increase of Cu content. For the low Cu content sample, the hysteresis loop was slightly tilted which indicated that the diamagnetism coexisted in this sample. The temperature dependence of magnetization of Zn1-xCuxO revealed that the magnetic exchange coupling depended on the doping concentration of Cu and there were many different local environments for magnetism. The measured hysteresis loop and temperature dependence of magnetization were overall performance of the magnetism coming from a wide distribution of ferromagnetic exchange couplings.
基金
Funded by the Natural Science Foundation of Fujian Province(No.2011J01014)
the National Natural Science Foundation of China(No.11074099)