摘要
用光学多道分析器和微机控制线性升温法研究了MgSO4 :Dy和MgSO4 :Dy ,Mn热释光材料的发光光谱。测定不同温度和波长的发光光谱 ,得到了热释光三维光谱图。观察到MgSO4 掺入稀土元素Dy的两个发光谱带为 4 80nm和 580nm ,每个光谱带有多个发光峰。与掺入Dy的Ca SO4 的三维发光谱相比较 ,掺入稀土元素Dy的热释光材料的发光谱带的波长主要取决于掺入Dy3+的能级间的跃迁。MgSO4 同时掺入Dy和Mn后 ,4 80nm发光谱带受到很大的抑制 ,所有发光峰的发光效率显著减小 ;波长为 580nm谱带的多个发光峰中 ,温度低于 30 0℃的发光峰的发光效率显著减小 ,在 380℃附近的发光峰的发光强度最大。这说明掺入Mn杂质后 ,不同深度的陷阱的相对分布发生了变化。
Emission spectra of phosphor MgSO 4 doped with Dy and Dy/Mn were measured with an optical multichannel analyzer and a linear heating system whose temperature was controlled by a microcomputer. The emission spectrum bands at 480 nm and 580 nm of phosphor MgSO 4 doped with Dy were observed in the three dimensional (3D) glow curves. Compared with the 3D spectrum of CaSO 4:Dy and the spectrum bands of MgSO 4:Dy shows the same wavelengths which resulted from the quantum transitions among the energy levels of Dy 3+ ions. The intensities of the glow peaks in both spectrum bands (480nm and 580nm) of phosphor MgSO 4 doped with Dy/Mn were dramatically reduced except the 380℃ glow peak.
出处
《核技术》
CAS
CSCD
北大核心
2001年第1期1-5,共5页
Nuclear Techniques
基金
国家自然科学基金! (19775 0 71)
广东省自然科学基金资助项目