摘要
研究了钴盐品种和用量对NR胶料性能及子午线轮胎帘布胶 镀铜钢丝帘线粘合力的影响。结果表明 ,加入不同品种钴盐的胶料性能无明显差别 ;随着过硫化时间的延长 ,含钴盐CN 10和CN 16的胶料与镀铜钢丝帘线之间的粘合力明显下降 ;经热空气老化后不同品种钴盐均保持较好的耐热性能 ;经湿热蒸汽老化后钴盐CN 2 0 5和 6 80C具有较高的粘合力保持率。随着钴盐CN 2 0 5用量的增大 ,可获得较高的初始粘合力 ,但耐热空气老化和耐湿热蒸汽老化性能下降明显 ,其用量以 0 7~ 1
The effect of cobalt salt type and level on the properties of NR compound and the adhesion strength between the cord compound and the brass plated steel cord in radial tire was investigated.The results showed that the cobalt type had little effect on the compound properties;the adhesion strength between the CN 10 (cobalt naphthenate) containing compound or CN 16 (cobalt stearate) containing compound and the brass plated steel cord decreased significantly as the overcure time increased;the compounds with different types of cobalt salts had better heat resistance after heat air a ging;and the compounds with CN 20 5 (cobalt neodecanoate) or 680C (cobalt boroacylate) had higher adhesion strength retention after steam aging.The higher original adhesion strength could be obtained,but the heat air aging properties and steam aging properties decreased significantly as the level of CN 20 5 increased;and the optimal balanced adhesion properties were obtained when 0 7~1 2 phr of cobalt salt was used.
出处
《轮胎工业》
CAS
2001年第4期215-219,共5页
Tire Industry
关键词
钴盐
子午线轮胎
帘布胶
纲丝帘子线
粘合力
cobalt salt
radial tire
cord compound
steel cord
adhesion strength