摘要
通过对辐射室炉管的失效分析 ,阐明了炉管的失效部位、失效形式、失效原因及其影响因素 ,为采取有效的防护措施提供了依据。
By the analysis of the failure of radiation tubes, the location of failure, form of failure, the causes of failure and affecting factors were discussed, which provided the basis for adopting the effective corrosion protection measures.
出处
《石油化工腐蚀与防护》
CAS
2001年第1期30-32,64,共4页
Corrosion & Protection In Petrochemical Industry
关键词
延迟焦化
立式加热炉
炉管失效
高温氧化
渗碳腐蚀
高温硫腐蚀
delayed coker, furnace, tube failure, high-temperature oxidation, carburizing corrosion, high-temperature sulfur corrosion