研究了CaZr4（PO4）6（CZP）基复相陶瓷的抗热震性，在CZP中引入Al2O310wt％、ZrSiO420wt％后，临界淬冷温差提高，采用SEM对断口形貌进行了分析。
Thermal shock resistance of CaZr4(PO4)6(CZP) - based diphase ceramics were studied. The critical quenching temperature difference of CZP -based diphase ceramics were increased by adding Al2O310wt % .ZrSiO420wt% to CZP matrix ceramics respectively. The fractography of CZP - based diphase ceramics were analysed with the aid of SEM.