Monodispersed polystyrene latexes (100～500 nm) were prepared using seed emulsion polymerization.Hard and ordered polystyrene colloidal crystals were obtained by ambient drying the monodispersed polystyrene dispersions.Polystyrene colloidal crystals were chemically modified by controlled sulfonation with sulfuric acid to derive a novel macro ordered hydrogels including ordered hydrogels and core/shell hydrogels,in which sulfuric acid and sulfone groups are responsible for the hydrophilic and crosslinking performances,respectively.The chemical structure and morphologies of the hydrogels were characterized by FT IR.It is shown that at a given concentration of sulfuric acid,the structural features of the samples are controlled by sulfonation time and temperature.The modification starts from the outer layer of polystyrene spheres of the colloidal crystals and increases both in reaction rate and sulfone group amount with temperature.A preliminary mechanism of the sulfonation process to prepare the ordered structures was proposed.
Monodispersed polystyrene latexes (100～500 nm) were prepared using seed emulsion polymerization.Hard and ordered polystyrene colloidal crystals were obtained by ambient drying the monodispersed polystyrene dispersions.Polystyrene colloidal crystals were chemically modified by controlled sulfonation with sulfuric acid to derive a novel macro ordered hydrogels including ordered hydrogels and core/shell hydrogels,in which sulfuric acid and sulfone groups are responsible for the hydrophilic and crosslinking performances,respectively.The chemical structure and morphologies of the hydrogels were characterized by FT IR.It is shown that at a given concentration of sulfuric acid,the structural features of the samples are controlled by sulfonation time and temperature.The modification starts from the outer layer of polystyrene spheres of the colloidal crystals and increases both in reaction rate and sulfone group amount with temperature.A preliminary mechanism of the sulfonation process to prepare the ordered structures was proposed.
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2001年第5期561-563,共3页
Acta Polymerica Sinica
基金
国家自然科学基金资助项目 (基金号 2 0 0 2 30 0 3)
中科院化学所分子科学中心创新基金资助项目