采用熔融接枝的方法 ,制备了 (HDPE/LDPE) -g -GMA(甲基丙烯酸缩水甘油脂 )接枝物 ,研究了引发剂的用量、GMA的用量、苯乙烯 (St) /GMA的配比、转速、反应时间等因素对接枝率的影响。确立了最佳的接枝配方和工艺条件 :过氧化二异丙苯 (DCP)用量 0 1份、GMA用量 3份、St用量 3份、温度 180℃、转速 60r/min、反应时间为 10min。接枝反应动力学曲线与接枝反应过程的机理和特征相吻合。红外光谱的分析结果表明GMA确实接到了大分子链上 ;DTA分析结果表明 ,接枝物中GMA的引入导致大分子链的规整性降低 ,熔融温度略有下降。
HDPE/LDPE)-g-GMA is prepared by melt grafting.Effects of initiators and GMA dosages,St/GMA ratios,rotating speeds and reaction times on grafting yield are studied.Optimum formulation and processing parameters are DCP 0.1 phr,GMA 3 phr and St 3 phr,together with temperature of 180 ℃,rotating speed of 60 r/min and reaction time of 10 minutes.Reaction kinetics accords with mechanism and characteristic of grafting reaction.Melt grafting of GMA onto HDPE/LDPE blend is proved by FT-IR.DTA shows that introduction of GMA to HDPE/LDPE-g-GMA lowers the regularity of molecular chain, thus decreasing the melting temperature.