ZrO_2掺杂CeO_2基电解质材料的研究

The effects of zirconia on conductivity ceria-based solid electrolytes

在 Ce O2 / Sm2 O3体系中加入 Zr O2 ,能降低 Ce O2 基电解质材料的电导率 ,主要是因为Zr O2 的固溶使得 Ce O2 基电解质材料的晶格常数减小 ,活化能增加 ;添加 Zr O2 可提高材料的断裂强度 ,使材料断裂以穿晶断裂为主 ,同时可促进致密烧结 。

The addition of zirconia can improve the conductivity of the ceria electrolytes because the solid solution of ZrO 2 in CeO 2 can minish the crystal lattice constant and increase the activity energy.It can also improve the fracture strength of the electrolytes.