摘要
The A-type zeolite membrane was synthesized on a porous TiO 2 support by using dip-coating and microwave heating.The influence of chemical composition of precursor on the formation of zeolite membrane was investigated.The results showed that the concentration of the precursor determines the performance of zeolite membrane.The zeolite A crystals and the surface morphology of membrane were characterized by XRD and SEM.For the zeolite membrane,the particle size on its surface and the thickness of top-layer was about 0.5?μm and 1?μm,respectively.The permeability of H 2 and N 2 hardly changed with pressure and its permselectivity of H 2 to N 2 was about 5,more than that of Knudsen diffusion.It suggested that the zeolite A membrane exhibits partial molecular sieving.According to pervaporation measurements by using H 2O/EtOH mixture,the flux and selectivity of the A-type zeolite membrane for 5% H 2O/95% EtOH(mass) mixture at 323?K was 0.335?kg·m -2 ·h -1 and 690,respectively.
The A-type zeolite membrane was synthesized on a porous TiO 2 support by using dip-coating and microwave heating.The influence of chemical composition of precursor on the formation of zeolite membrane was investigated.The results showed that the concentration of the precursor determines the performance of zeolite membrane.The zeolite A crystals and the surface morphology of membrane were characterized by XRD and SEM.For the zeolite membrane,the particle size on its surface and the thickness of top-layer was about 0.5?μm and 1?μm,respectively.The permeability of H 2 and N 2 hardly changed with pressure and its permselectivity of H 2 to N 2 was about 5,more than that of Knudsen diffusion.It suggested that the zeolite A membrane exhibits partial molecular sieving.According to pervaporation measurements by using H 2O/EtOH mixture,the flux and selectivity of the A-type zeolite membrane for 5% H 2O/95% EtOH(mass) mixture at 323?K was 0.335?kg·m -2 ·h -1 and 690,respectively.
出处
《化工学报》
EI
CAS
CSCD
北大核心
2001年第8期749-752,共4页
CIESC Journal