摘要
采用两种管线钢材料 ,通过再结晶区和未再结晶区的五道次变形将试样厚度从 6 0 mm轧为 8mm。热轧后的试样进行水幕冷却 ,然后分别放置于 5 0 0℃和 40 0℃的加热炉中随炉冷却以模拟卷取。结果表明 。
Two pipe line steel specimens with 60 mm thickness were deformed to 8 mm thickness in five passes in either recrystallized or non recrystallized austenite regions subsequent to austenitization at 1200 ℃ After hot rolling, the specimens were spray water cooled and then furnace cooled from 500 ℃ and 400 ℃ to simulate coiling process The result shows that under the appropriate cooling process, the microstructure that contains mainly acicular ferrite could be obtained in all the two steels
出处
《钢铁》
CAS
CSCD
北大核心
2001年第9期46-49,共4页
Iron and Steel
基金
国家重大基础研究资助项目 ( G19980 6 15 11)