To obtain a novel support with practical value for metallocene catalyst(\%η\%\|C\-5H\-5)TiCl\-3(CpTiCl\-3), poly(styrene\|co\|4\|vinylpyridine)/SiO\-2 nanoscale hybrid material(SrP/SiO\-2) was firstly produced as support. After pretreatment by methylaluminoxane(MAO), the hybrid materials reacted with CpTiCl\-3. The results from SAXS, SEM and TEM indicated the morphology and structure of organic/inorganic hybrid materials, and the size of inorganic particle in hybrid was nanoscale. The results from IR and XPS showed that there were two possible cationic active species in the hybrid\|supported catalyst, the polymerization results of styrene proved this possibility.
To obtain a novel support with practical value for metallocene catalyst(\%η\%\|C\-5H\-5)TiCl\-3(CpTiCl\-3), poly(styrene\|co\|4\|vinylpyridine)/SiO\-2 nanoscale hybrid material(SrP/SiO\-2) was firstly produced as support. After pretreatment by methylaluminoxane(MAO), the hybrid materials reacted with CpTiCl\-3. The results from SAXS, SEM and TEM indicated the morphology and structure of organic/inorganic hybrid materials, and the size of inorganic particle in hybrid was nanoscale. The results from IR and XPS showed that there were two possible cationic active species in the hybrid\|supported catalyst, the polymerization results of styrene proved this possibility.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2001年第12期2117-2119,共3页
Chemical Journal of Chinese Universities
基金
国家重点基础研究专项经费 ( G19990 6 480 1)
中国科学院院长基金资助